TECHNICAL DATA FOR RECYCLED PLASTIC
The following results were obtained using a standard 3-point test carried out on the 140mm x 38mm solid profile.
| Parameter | Description / Units | Result |
| DENSITY | g/mm³ | 0.93 |
| FLEXURAL STRENGTH | Max Flexural stress sustained by the specimen which caused it to rupture. Megapascals - ( Mpa) | 21 |
| MODULUS of ELASTICITY |
Mpa | 889 |
| IMPACT ENERGY | Impact required to rupture the specimen during the 3 point bending test. Millijoules - ( Mj) | 346 |
| MAXIMUM DEFLECTION | The maximum downward deflection prior to breaking. ( mm) | 125 |
| Method used conforms in broad principle to ISO 178:1993 (E) | ||
| WATER ABSORPTION | IS0 62 : 1980 (E) | -0.67% |
LABORATORY REPORT.
SALT TEST ON 140mm x 38mm SECTION.
The method used conforms to ASTM B117 (1000 hrs under a constant fog spray of 5% salt solution.)
RESULT: No discernible effect on sample.
SLIP RESISTANCE TESTS.
The method used conforms to BS 7976-2:2002, using a Four-S rubber slider pad.
| Sample used | 140mm x 38mm decking |
|
| Temperature and Condition | 20° (Dry) |
20° (Wet) |
| Pendulum Test Value Surface | 72 |
54 |
Rapra Technology issued the following slip resistance guidance in January 1996:
| Classification of Flooring | P. T. V. (Four S rubber) |
| Dangerous | 24 and below |
| Marginal | 25 - 34 |
| Satisfactory | 35 - 64 |
| Excellent | 65 and above ** |